Product Details:
| ASTM | 1085 |
| Shape | Round |
| Silicon | 0.17 -0.37% |
| Size Range | 2.0mm - 25.4mm |
| Grades | G48 - G1000 |
| AISI | 302 |
| Chemical Composition | |
| Carbon | 0.8 -0.92% |
| Manganese | 0.70 -1.0% |
| Silicon | 0.17 -0.37% |
| Sulphur | 0.05% max. |
| Phosphorous | 0.04% max. |
| General Usage | |
| Take high load and provide longer life than case hardened carbon balls, applications is the cycle industry, food industry, etc. |
| Material Conversion: | ||||
| ASTM/AISI | DIN | W-Nr. | NF | JIS |
| 1085 | CK85 | 1.1269 | XC85 | SUP3 |
Product Details:
| Ball Diameter | 2.0-3.0mm to 6.6-9.5mm |
| Minimum Case Depth | 1.4mm to 2.0mm |
| Hardness | HRC 60 min |
| Size Range | 2.0mm to 50mm |
| Grades | G48 - G1000 |
| AISI | 302 |
| Chemical Composition | |
| Carbon | 0.12-0.18 % |
| Manganese | 0.30-0.60% |
| Silicon | 0.17 — 0.37% |
| Sulphur | 0.0 3 5% max. |
| Phosphorous | 0.0 3 5% max. |
| Mechanical Properties | |
| Tensile Strength | 325,000 psi |
| Yield Strength | 295,000 psi |
| Modulus of Elasticity | 29,500,000 psi |
| Density | 0.284 cb./cu. in. |
| Physical Characteristics | |
| Hardness | HRC 60 min |
| General Usage | |
| Moderate loads and alow rotating parts, for example: castors, conveyors, roller skates, drawer slides, seat slides, bicycles,etc. |
| Case Depth | |||||
| Ball Diameter | 2.0-3.0mm | 3.1-4.5mm | 4.6-5.5mm | 5.6-6.5mm | 6.6-9.5mm |
| Minimum Case Depth | 0.5mm | 0.6mm | 0.8mm | 0.9mm | 1.1mm |
| Ball Diameter | 9.5-11.0mm | 11.1-12.5mm | 12.6-14.0mm | 14.1-19.0mm | 19.1-38.0mm |
| Minimum Case Depth | 1.4mm | 1.7mm | 1.8mm | 1.9mm | 2.0mm |
Product Details:
| Material | Brass |
| Hardness | RB 75-87 |
| Customisation | Customised |
| Size Range | 2mm to 16mm |
| Grades | 25, 100, 200, 500, 1000 |
| Brass | CDA 260 |
We are well-reckoned Brass Balls Manufacturer, Exporter and Supplier. Non-ferrous in nature, the Brass Balls exhibit excellent electrical conductivity and corrosion resistance.
Brass balls are placed under the category of non-ferrous balls. They provide excellent resistance to corrosion by water, and are substantially lower in cost than other corrosion-resisting balls. Brass balls are frequently used in many types of valve applications requiring small-size ball
| Chemical Composition | |
| Copper | 0.70% |
| Zink | 0.30% |
| Mechanical Properties | |
| Hardness | RB 75-87 |
| Surface Finish | -8 Micro Finish |
| Physical Characteristics | |
| Corrosion Resistance | Yes |
| General Usage | |
| Valves, Electronics, Automotive Security, Appliances | |